18 Years Factory Denstone Ceramic Balls - Inert Middle Alumina Balls – Catalyst Support Media – Kelley
18 Years Factory Denstone Ceramic Balls - Inert Middle Alumina Balls – Catalyst Support Media – Kelley Detail:
Application
They are widely used in many fields, including petroleum, chemical engineering, fertilizer production, natural gas and environmental protection. They are used as covering and supporting materials of catalysts in reaction vessels and as packing in towers.
Chemical Composition
Al2O3+SiO2 | Al2O3 | Fe2O3 | MgO | K2O+Na2O +CaO | Others |
> 93% | 45-50% | <1% | <0.5% | <4% | <1% |
Physical Properties
Item |
Value |
Water absorption (%) |
<2 |
Bulk density (g/cm3) |
1.4-1.5 |
Specific gravity (g/cm3) |
2.4-2.6 |
Free volume (%) |
40 |
Operation temp.(max) (℃) |
1200 |
Moh’s hardness (scale) |
>7 |
Acid resistance (%) |
>99.6 |
Alkali resistance (%) |
>85 |
Crush Strength
Size |
Crush strength |
|
Kgf/particle |
KN/particle |
|
1/8”(3mm) |
>25 |
>0.25 |
1/4”(6mm) |
>60 |
>0.60 |
3/8”(10mm) |
>80 |
>0.80 |
1/2”(13mm) |
>230 |
>2.30 |
3/4”(19mm) |
>500 |
>5.0 |
1”(25mm) |
>700 |
>7.0 |
1-1/2”(38mm) |
>1000 |
>10.0 |
2”(50mm) |
>1300 |
>13.0 |
Size and Tolerance (mm)
Size |
3/6/9 |
9/13 |
19/25/38 |
50 |
Tolerance |
±1.0 |
±1.5 |
±2 |
±2.5 |
Product detail pictures:
Related Product Guide:
We are proud of the high customer satisfaction and wide acceptance due to our persistent pursuit of high quality both on product and service for 18 Years Factory Denstone Ceramic Balls - Inert Middle Alumina Balls – Catalyst Support Media – Kelley, The product will supply to all over the world, such as: Danish, Cologne, Ghana, Due to our dedication, our products are well known throughout the world and our export volume continuously grows every year. We will continue to strive for excellence by providing high quality products that will exceed the expectation of our customers.
By Chloe from Pretoria - 2017.12.02 14:11
Problems can be quickly and effectively resolved, it is worth to be trust and working together.
By David from Riyadh - 2018.02.08 16:45